Photo-mask blank for use in lithography including a modified chromium compound

ABSTRACT

In a photo-mask blank, a transparent substrate is covered with a shading layer including chromium and chromium carbide. On the shading layer is an antireflection layer which includes chromium and chromium nitride. The shading and the antireflection layers are deposited in the same hollow space by sputtering. The etch rate of the shading layer is adjustable to that of the antireflection layer to make both etch rates equal and, thereby, to reduce undercuts appearing at the shading layer.

This application is a continuation of application Ser. No. 357,878, filed Mar. 15, 1982, abandoned.

BACKGROUND OF THE INVENTION

This invention relates to a photo-mask blank for use in lithography.

In general, a photo-mask blank of the type described is selectively etched or processed into a mask indispensable to the lithography technique of semiconductor integration. As a photo-mask blank, well-known is a chromium mask blank comprising a transparent glass substrate and a shading layer of chromium for shading incident light thereon.

In order to reduce the intensity of light reflected from the shading layer, the chromium mask blank very often comprises an antireflection layer of chromium oxide coated on the shading layer. The latter blank has a low reflectance, namely, a low reflection index and will, therefore, be referred to as a low reflection blank hereinafter.

In any event, the photo-mask blank is covered with a photo-resist layer on fabrication of the mask to delineate patterns on the photo-mask blank.

A conventional low reflection blank is manufactured by coating, in turn, the shading layer of chromium and the antireflection layer of chromium oxide on the transparent substrate by the use of sputtering and/or vacuum evaporation. As will later be described with reference to the figures of the accompanying drawing, the conventional low reflection blank exhibits a relatively high reflection index except a predetermined wavelength region when it is uncovered and covered with the photoresist layer. Therefore, the conventional low reflection blank inevitably imposes restrictions on the usable wavelength region.

Furthermore, the conventional low reflection blank is disadvantageous in that the shading layer of chromium is etched by an etchant faster than the antireflection layer of chromium oxide covered on the shading layer on fabrication of the mask. As a result, undercuts take place at the shading layer underlying an edge of the antireflection layer. This makes it difficult to delineate fine patterns on the glass substrate.

SUMMARY OF THE INVENTION

It is an object of this invention to provide a photo-mask blank for use in a lithography technique, which is capable of reducing undercuts on fabrication of a mask.

It is another object of this invention to provide a photo-mask blank of the type described, wherein the reflection index is invariable over a broad wavelength of light.

It is yet another object of this invention to provide a photo-mask blank of the type described, which is capable of delineating fine patterns.

It is still another object of this invention to provide a photo-mask blank covered with a shading, layer and an antireflection layer on the shading layer, wherein the shading layer and the antireflection layer are continuously formed in an identical hollow space.

It is another object of this invention to provide a method of the type described, which is capable of adjusting an etch rate of a shading layer to that of an antireflection layer.

A photo-mask blank to which this invention is applicable is for use in lithography and comprises an optically transparent substrate having a principle surface and a shading layer on the principal surface for shading light in a predetermined wavelength region. According to this invention, the shading layer includes chromium and chromium carbide to provide coexistence of the chromium and the chromium carbide. The photo-mask blank further comprises an antireflection layer including chromium oxide and chromium nitride. The etch rate of the shading layer is not higher than that of the antireflection layer and undercuts are suppressed at the shading layer.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 shows a graph of reflection index versus wavelength characteristics of a conventional photo-mask blank;

FIG. 2 shows a fragmentary cross section of a photo-mask blank according to this invention;

FIG. 3 shows a similar view of a photo-mask blank according to a preferred embodiment of this invention; and

FIG. 4 shows a graphical representation of characteristics of the photo-mask blank illustrated in FIG. 3.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Referring to FIG. 1, wherein the abscissa and the ordinate represent wavelength (nanometers) and reflection index (percent), respectively, description will be made of a conventional low reflection blank for a better understanding of this invention. The conventional low reflection blank comprises a thoroughly polished glass substrate, a metal layer of chromium formed on the glass substrate to a thickness of about 800 angstroms, and a chromium oxide layer formed on the metal layer to a thickness of about 250 angstroms. The metal and the chromium oxide layers serve as a shading and an antireflection layer, respectively. The metal layer is formed at a deposit rate of about 35 angstroms per second in an argon atmosphere of 5×10⁻³ Torr by the use of a d.c. sputter device of a planar magnetron type. The d.c. sputter device was adjusted so that the metal layer to be formed became equal in optical density to 3.0. On the other hand, the chromium oxide layer was coated onto the metal layer at the deposit rate of 1 angstrom per second in an oxygen atmosphere of about 1×10.sup. -4 Torr by the use of an evaporation device.

In FIG. 1, a curve 11 shows a reflection index versus wavelength characteristic of the conventional photo-mask blank without a photoresist layer. The reflection index was measured by a known spectrometer above the antireflection layer, namely, chromium oxide layer. As readily understood from curve 11, the conventional mask blank per se exhibits a low reflection index in a wavelength region below 500 nanometers. A curve 12 shows a similar characteristic of the conventional blank covered with a photoresist layer. The photoresist layer consists of AZ-1350 manufactured and sold by Shipley Far East Ltd., Tokyo, Japan. As shown by the curve 12, the reflection index is widely varied and locally exceeds twenty percent even in the wavelength region below 500 nanometers when the photoresist layer is coated on the conventional blank. Inasmuch as the photoresist layer should be exposed to light having a predetermined wavelength less than 500 nanometers so as to delineate mask patterns on fabrication of a mask, resolution of an image is inevitably deteriorated, if the reflection index exceeds twenty percent with the photoresist layer coated on the blank, as shown by the curve 12 in FIG. 1.

According to the inventors' experimental study, the metal layer of chromium was excessively etched by an etchant as compared with the chromium oxide layer and, as a result, undercuts inevitably occur at the metal layer underlying an edge of the chromium oxide layer. In practice, use was made, as the etchant, of a solution of 1000 milliliters formed by adding distilled water to 165 grams of ceric ammonium nitrate and 42 milliliters of perchloric acid (70%). Etching was carried out for twenty seconds, with the solution kept at 19°-20° C. It is mentioned here that the amount of undercuts can quantitatively be defined by a side etch rate representative of a reduction rate of a pattern width for ten seconds. As regards the conventional low reflection blank, the side etch rate thereof was about 0.20 micron per ten seconds.

Referring to FIG. 2, a chromium mask blank according to an embodiment of this invention comprises a thoroughly polished glass substrate 15 transparent to light in a predetermined wavelength region and having a principal surface. The predetermined wavelength region may at least include a wavelength region between 350 and 600 nanometers and may, of course, include a region from the ultraviolet region to the infrared region.

A shading layer 16 is on the principal surface and includes chromium and chromium carbide dispersed in the chromium. The shading layer 16 serves to shade the light in the predetermined region. Practically, the shading layer 16 of chromium and chromium carbide shades the light from the ultraviolet region to the infrared region. The chromium and the chromium carbide may coexist in the form of an interstitial carbide of chromium in the shading layer 16. The chromium carbide may be unequally dispersed in the shading layer 16. Thus, the chromium mask blank illustrated in FIG. 2 includes a modified chromium compound in the form of chromium carbide in the shading layer 16.

The shading layer 16 was deposited by the use of a d.c. sputtering device of a planar magnetron type known in the art. More particularly, the substrate 15 was located in a hollow space defined by a chamber or belljar (not shown) of the sputtering device, along with a target of chromium. The hollow space was filled with a mixed gas including argon and methane (CH₄) after evacuation by an exhausting system in the usual manner. At this time, total pressure of the hollow space was kept at about 1×10⁻³ Torr.

Under these circumstances, reactive sputter was carried out by sputtering particles of the target onto the substrate 15 to deposit the shading layer 16 including the chromium and the chromium carbide. The chromium carbide in the shading layer 16 results from reaction of the sputtered particles of chromium with carbon included in the methane. During sputter, the sputtering device was adjusted so that the optical density of the deposited layer became equal to 3.0. It has been confirmed that the deposited shading layer 16 shades light from the substrate 15.

Various photo-mask blanks were experimentally manufactured to seek relationships between the etch rate and a mixed ratio of the argon and the methane. The relationships are listed in Table 1 below. In Table 1, the shading layers according to this invention are labelled A, B, C, and D while the conventional shading layer is shown at E.

                  TABLE 1                                                          ______________________________________                                         Mixed Ratio                                                                    (by volume)                                                                               Thickness   Etching   Etch Rate                                     Ar:CH.sub.4                                                                               (Å)     Time (sec)                                                                               (Å/sec)                                   ______________________________________                                         A   95      5      560       36      16                                        B   90     10      570       45      13                                        C   85     15      575       56      10                                        D   80     20      580       66       9                                        E   100     0      550       24      23                                        ______________________________________                                    

As readily understood from Table 1, the shading layer (shown at E) including no chromium carbide is faster in etch rate than the shading layers (shown at A-D) including chromium carbide. The etch rate is gradually reduced with an increase of the methane in the mixed gas. Accordingly, it is possible to attain various kinds of shading layers with different etch rates by changing the mixed ratio of the argon and the methane.

Referring to FIG. 3, a low reflection blank according to a preferred embodiment of this invention comprises similar parts designated by like reference numerals. The shading layer 16 is applied to the substrate 15 in a manner similar to that illustrated with reference to FIG. 2 and, consequently, includes the coexistence of chromium and chromium carbide. Specifically, the shading layer 16 was deposited onto the substrate 15 to a thickness of 570 angstroms by the sputtering device described with reference to FIG. 2. Reactive sputter was carried out in the mixed gas of the argon and the methane which included, by volume, 90% of the argon and 10% of the methane.

The low reflection blank further comprises an antireflection layer 17 including chromium oxide and chromium nitride to provide coexistence of the chromium oxide and chromium nitride. Thus, the chromium oxide in the antireflection layer is subjected to modification by the chromium nitride. The chromium nitride may be unequally dispersed in the chromium oxide.

The antireflection layer 17 was deposited onto the shading layer 16 to a thickness of about 250 angstroms by the sputtering device in a mixed gas including, by volume, 80% of argon and 20% of nitrogen monoxide. The total pressure of the mixed gas was about 1.3×10⁻³ Torr. Deposition of the antireflection layer 17 continuously followed deposition of the shading layer 16 in the same hollow space. No contamination takes place on the shading layer 16 and the antireflection layer 17 because the substrate 15 is not moved in the atmosphere and no dust which would accompany movement of the substrate 15 becomes attached to the substrate 15. It took about 43 seconds to etch both the shading and the antireflection layers 16 and 17 deposited in the above-mentioned manner, by the etchant described with reference to FIG. 1. The side etch rate was equal to 0.06 micron per ten seconds.

From this fact, it is readily understood that the side etch rate is reduced in the low reflection blank according to this invention in comparison with the conventional blank described with reference to FIG. 1. Inasmuch as the etch rate of the antireflection layer is approximately equal to that of the shading layer, occurrence of undercuts can favorably be reduced at the shading layer underlying the edge of the antireflection layer. Further, the etch rate of the shading layer 16 is adjustable to that of the antireflection layer 17 by changing the ratio of argon and methane. This means that the shading layer may be deposited with reference to the etch rate of the antireflection layer to be formed on the shading layer.

Referring to FIG. 4, the low reflection blank illustrated in conjunction with FIG. 3 has a reflection index versus wavelength characteristic as shown by curve 21, without a photoresist layer on the blank. As regards the wavelength region between 400 and 500 nanometers, a maximal value of the curve 21 reaches about 11% while that of the curve 11 illustrated in FIG. 1, about 10%. Therefore, the low reflection blank according to this invention is somewhat higher in reflection index than the conventional mask blank in the wavelength region between 400 and 500. It will, however, be seen that the low reflection blank according to this invention exhibits a reflection index less than 20% in the broad wavelength region between 350 and 600 nanometers and is flat in the characteristic as compared with the conventional blank described with reference to FIG. 1. Thus, the antireflection layer 17 serves to reduce reflection of light in at least a part of the predetermined wavelength region.

In FIG. 4, curve 22 shows the reflection index versus wavelength characteristic when the low reflection blank according to this invention is covered with the photoresist layer of AZ-1350 described before. As shown by the curve 22, the reflection index never exceeds 30% even in the wavelength region exceeding 600 nanometers. The low reflection blank illustrated in FIG. 3 exhibits a low and uniform reflection index over a wide wavelength region. This means that the mask blank is also useful in the wavelength region above 600 nanometers.

According to this invention, it is possible to improve the reflection index versus wavelength characteristics in addition to the etch rate of the shading layer. Thus, fine patterns can be precisely delineated with the shading and the antireflection layers selectively remaining on the substrate 15. It is, therefore, possible to fabricate, by selectively etching the shading and the antireflection layers, a mask having precise and fine patterns without substantial undercuts of the shading layer 16. In other words, the mask according to this invention comprises the antireflection layer remaining and superposed only on the selectively remaining shading layer.

While this invention has thus far been described in conjunction with a few embodiments thereof, it is readily possible for those skilled in the art to practice this invention in various ways. For example, various kinds of gases may be used to deposit the shading layer, instead of the mixed gas of argon and methane. The substrate may be of quartz and/or may comprise a transparent flat plate covered with a conductive and transparent film of a material, such as indium oxide, stannic oxide or the like, which defines the principal surface. 

What is claimed is:
 1. A photo-mask blank for use in lithography comprising a substrate transparent to light in a predetermined wavelength region and having a principal surface, a shading layer on said principal surface which includes chromium and chromium carbide for shading the light in said predetermined wavelength region, and an antireflection layer overlaid on said shading layer which includes chromium oxide and chromium nitride for reducing reflection of the light in at least a part of said predetermined wavelength region.
 2. A photo-mask blank as claimed in claim 1 wherein said shading layer and said antireflection layer have substantially equal etch rates.
 3. A photo-mask blank as claimed in claim 1 constituted as a composite consisting of said substrate with said shading layer and said antireflection layer applied thereto as a two-layer covering.
 4. A photo-mask blank as claimed in claim 1 wherein said shading layer consists essentially of said chromium and chromium carbide and said anti-reflection layer consists essentially of chromium oxide and chromium nitride.
 5. A photo-mask blank as claimed in claim 4 wherein said shading layer is sputter deposited on said substrate and said anti-reflection layer is sputter deposited on said shading layer.
 6. A photo-mask blank as claimed in claim 1, said blank having a relatively flat characteristic of reflection index (%) vs wavelength (nm) in the region of 350-600 nm in which the reflection index is between 11 and 20%.
 7. A photo-mask blank as claimed in claim 6 wherein the reflection index has a minimum value at a wavelength between 400 and 500 nm.
 8. A photo-mask blank as claimed in claim 1 wherein the chromium and chromium carbide of the shading layer coexist in the form of interstitial chromium carbide.
 9. A photo-mask blank as claimed in claim 1, wherein said substrate is glass.
 10. A photo-mask blank as claimed in claim 1, wherein said substrate is quartz.
 11. A photo-mask blank as claimed in claim 1, wherein said substrate comprises a transparent flat plate and a conductive and transparent film on said transparent flat plate to provide said principal surface.
 12. A photo-mask for use in lithography comprising a substrate transparent to light in a predetermined wavelength region and having a principal surface, a shading layer selectively remaining on said principal surface which includes chromium and chromium carbide for shading the light in said predetermined wavelength region, and an antireflection layer only on said shading layer which includes chromium oxide and chromium nitride for reducing reflection of light in at least a part of said predetermined wavelength region.
 13. A photo-mask as claimed in claim 12 wherein said shading layer and said antireflection layer have substantially equal etch rates.
 14. A photo-mask as claimed in claim 13 wherein said shading layer and antireflection layer are substantially coextensive without undercuts in said shading layer.
 15. A photo-mask as claimed in claim 12 constituted as a composite consisting of said substrate with said shading layer and said antireflection layer applied thereto as a two-layer covering.
 16. A photo-mask as claimed in claim 12 wherein said shading layer consists essentially of said chromium and chromium carbide and said anti-reflection layer consists essentially of chromium oxide and chromium nitride.
 17. A photo-mask as claimed in claim 16 wherein said shading layer is sputter deposited on said substrate and said anti-reflection layer is sputter deposited on said shading layer.
 18. A photo-mask as claimed in claim 12, said photo-mask having a relatively flat characteristic of reflection index (%) vs wavelength (nm) in the region of 360-600 nm in which the reflection index is between 11 and 20%.
 19. A photo-mask as claimed in claim 18 wherein the reflection index has a minimum value at a wavelength between 400 and 500 nm.
 20. A photo-mask as claimed in claim 12 wherein the chromium and chromium carbide of the shading layer coexist in the form of interstitial chromium carbide. 